NCS Profile Book

PROFILE BOOK

TABLE OF CONTENTS

SECTION I SECTION II SECTION III SECTION IV SECTION V SECTION VI SECTION VII SECTION VIII SECTION IX SECTION X

ANTI-ABRASION PROFILES ANTI-CORROSION PROFILES FLOOR PROFILES MARINE PROFILES PIPELINE PROFILES PRIMARY CONTAINMENT PROFILES ROOF PROFILES SECONDARY CONTAINMENT PROFILES WATERPROOFING PROFILES MISCELLANEOUS PROFILES

NUKOTE COATING SYSTEMS 629 LINGLING ROAD / AIHE MANSION SUITE 7H SHANGHAI, CHINA 200030 TEL: +8621-5424-9811 / FAX: +8621-5424-9815 www.nukote-asia.com

NUKOTE PROJECT PROFILES
ANTI-ABRASION APPLICATIONS

NUKOTE COATING SYSTEMS 629 LINGLING ROAD / AIHE MANSION SUITE 7H SHANGHAI, CHINA 200030 TEL: +8621-5424-9811 / FAX: +8621-5424-9815 www.nukote-asia.com

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: RESULTS: Explosive Carriers Military AntiAbrasion Haliburton NA SS 1500 m2 1997 Excellent

Project Description: Transportation modules for explosives require both abrasion and corrosion resistance. Corrosion resistance is required for life expectancy of the modules as they encounter typical explosive chemical corrosives. More important is the ability of the coating to withstand abrasion and eliminate the hazard of sparks generated by abrasion against metal surfaces. Nukote Polyureas provide the solution to both issues and were utilized to coat both the interiors and exteriors of these special carriers. A high pigment red color was utilized with ultraviolet additives to extend physicals and provide color stability. The product was applied to sand blasted steel surfaces (encapsulation) over a suitable primer.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

PROJECT PROFILES

Project: Kidston Gold Mine Client: Placer Pacific Limited Distributor: Nukote Coating Systems Contractor: Ausbelt Ltd. Application Type: Abrasion-Corrosion Resistance Completion: 2001 Scope: The steel surface was abrasive blasted to a 2.5 mm profile and primed with suitable steel primers then an Aromatic Polyurea was applied to the derrick screens and under pans to protect the steel from both corrosion and abrasion. System: Surface Area: Completion Date: Results: After twelve months of continuous use, 24 hours per day 7-days per week, the surfaces were inspected and were found free from visible wear or other problems. Polyurea has replaced polyurethanes as the coating of choice at this mining facility. 6000 Microns of Nukote ST Aromatic Polyurea 150 m2 September 2001-2002-2003

SHANGHAI ♦ JAKARTA ♦ DUBAI ♦ SEATTLE ♦ DAFENG ♦ LONG BEACH www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: RESULTS: Airport Striping Transportation Anti-Abrasion Multiple NA Nukote-AL Various 2002 Excellent

Project Description: Airport runways are subject to aggressive abrasion resulting principally from airliner landings. The impact force and abrasion encountered is obvious visually and intellectually when the life expectancy of tires utilized by the airlines is reviewed. In 2001 testing and field trials were performed using AL product formulations to stripe runways in major airports within the United States with excellent results. Special equipment modifications were made to provide a simple consistent application thickness while ensuring straight even stripe lines. Since that time many airports have specified this coating system for their runway striping applications. AL safety yellow color is the product commonly specified due to its high abrasion resistance, color stability in ultraviolet exposure and chemical resistance to jet fuels.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: Carbon columns interior coating Mining Anticorrosion, abrasion resistance Pasminco Mining, Kidston gold mine Not available 3mm HT Tank interior 1998 October

INSPECTION RESULTS: Excellent, no visible failure JOB DESCRIPTION: The owner chose HT to resist the corrosive and abrasive conditions that exist on the interior of the carbon columns of their gold mine. The steel was cleaned with and abrasive and 3 mm of HT was applied. The down time was a large concern with the owners who were pleasantly surprised when their columns were coated and operational within hours.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: CRL Tankhouse Mining Acid and electrolyte anticorrosion MIM Copper Refineries, Townsville Not available 1-2 mm SS100 onto prepared concrete 1,100 m² 1998 June

OWNER:

CONTACT: SYSTEM:

COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent JOB DESCRIPTION: SS100 was chosen because of its ease of application, chemical and acid resistance, slip resistance, flexibility, and abrasion resistance. The minimized downtime was also a great advantage in choosing SS100. The concrete degradation was removed and replaced. SS100 was then applied onto a primed surface at a 1-2 mm dft.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: Fertilizer chutes Shipping and logistics Protective coating for equipment MIM Townsville Not available 1.5-2 mm Nukote HT 65 m² 1999 September

OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent JOB DESCRIPTION: load material onto boats. The header chutes were used at the Townsville port shipping facilities to

The owner required a non-stick, abrasion resistant, cost effective surface that would not only be maintenance free but also minimize cleaning time for personnel. The abrasive blasted surface was primed and then coated to a 1.5-2 mm dft.

For more pictures please see the following page

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: Mango washer Food processing Anticorrosion and abrasion resistance Burdekin Engineering Not available NUKOTE ST Multiple pieces of equipment 1999 February

OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent JOB DESCRIPTION: Nukote-ST was chosen for its chemical and abrasion resistance ability to coat machinery and equipment used in washing and treating mango fruit. Although ST was as tough as other coating options its flexibility helped reduce bruises to the fruit during processing. The owners are extremely pleased with the products performance and minimal maintenance requirements.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: Steel orifice plate protection Mining Anticorrosion, abrasion resistance Pasminco Mining, Kidston Gold Mine Not available HT Multiple plates 1998 August

OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent, no visible failure JOB DESCRIPTION: abrasion resistance. HT was chosen to coat steel orifice plate covers for anticorrosion and

The plates were abrasive blasted to a 2.5mm profile and primed with 302 primer. HT was applied at a 3 mm dft. The covers have performed extremely well in the rigorous, 24-hour production schedule of this mine.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

NUKOTE PROJECT PROFILES
ANTI-CORROSION APPLICATIONS

NUKOTE COATING SYSTEMS 629 LINGLING ROAD / AIHE MANSION SUITE 7H SHANGHAI, CHINA 200030 TEL: +8621-5424-9811 / FAX: +8621-5424-9815 www.nukote-asia.com

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: RESULTS: Project Description: The corrosive environments common to off shore drilling platforms are some of the toughest applications a coating can be subjected to. High exposures to salt spray combined with major temperature swings, constant ultra-violet exposures and the presence of hydrocarbons are typical conditions that must be addressed. Coatings utilized must also exhibit strong abrasion and impact resistance due to the working conditions encountered on these platforms. Nukote products provide solutions to the coating design requirements for these applications. Our polyurea products provide the durability, abrasion and corrosion resistance required in most applications. Where high temperatures and heavy hydrocarbon content are encountered, Admetal or composites of polyurea and Admetal provide the required solutions. Each application has specific temperature and corrosion requirements. These projects are also logistically challenging and in many cases require special explosion proof equipment systems. Contact your Nukote sales representative to develop a specific solution for your project. Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected] Off Shore Drilling Platforms Oil and Gas Anti-Corrosion Multiple Multiple Polyureas / Admetal Various Various Excellent

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: Aviation fuel hydrant pits Aviation Anticorrosion Anchorage International Airport Jack Hively, 001-907-248-5000 SS100 2 mm 200 hydrant pits 1990-1994

INSPECTION RESULTS: Excellent, some color change JOB DESCRIPTION: Jet fueling pits on the tarmac of Anchorage International Airport were sprayed with SS100 to prevent spilled fuel from leaking into the ground. SS100 was chosen because it was not only resistant to many chemicals and a variety of fuels, but also because it could be applied over a possibly contaminated substrate. SS100 was also ideal because of its ability to withstand extreme freeze-thaw cycles common to the Alaskan environment. The finished pits have performed excellently despite continued exposure to jet fuel, water, and antiicing agent. There is some change in color, but no breakdown in material. SS100 was applied onto concrete, geotextile fabric and directly onto the ground.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: Electrical insulation of cleats Mining Anti-corrosion Townsville Copper Refineries Not available 2 mm SS100 2,900 cleats
40mm x 2mm 70mm x

1998 September 7

INSPECTION RESULTS: Excellent JOB DESCRIPTION: Cleats are used in the construction of walkways passing through the electrolysis process. The cleats separate the walkways from the processing and prevent electrical hazard through conduction. The cleats were washed with mentholated spirits and laid out in overlapping rows with string separating each cleat to prevent joining during coating. The process was repeated to cover both sides.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: Containment of electrolyte pit and floors Mining Anti-corrosion Queensland Copper Refineries, Townsville Not available 2 mm ST 500+ m² 1998 July 29

INDUSTRY: USE: OWNER:

CONTACT: SYSTEM: COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent ST was chosen over existing polyethylene systems, which had JOB DESCRIPTION: previously failed allowing electrolyte and other acids to penetrate and contaminate the concrete. The contaminated concrete was scabbled out and topped with a cement repair mixture. The surface was primed with multiprime and then coated with ST with a 2 mm dft. The flexibility, toughness, acid resistance and minimum downtime enabled the area to be back in service within hours.

For more pictures please see the following page Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: Fertilizer chutes Shipping and logistics Protective coating for equipment MIM Townsville Not available 1.5-2 mm SS100 65 m² 1999 September

OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent JOB DESCRIPTION: load material onto boats. The header chutes were used at the Townsville port shipping facilities to

The owner required a non-stick, abrasion resistant, cost effective surface that would not only be maintenance free but also minimize cleaning time for personnel. The abrasive blasted surface was primed and then coated to a 1.5-2 mm dft.

For more pictures please see the following page

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: Land Cruiser Military, Australia Anti-corrosion Australian Military Craig Mason 0747-751033 SS100 HP/UV with a clear aliphatic top coat Entire car 1998 November 1

COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent SS100 was chosen as a protective coating to encapsulate the entire JOB DESCRIPTION: vehicle. Salt-water corrosion was the owners’ primary concern as the vehicle was repeatedly driven through salt water. The surface was abrasive blast cleaned, primed with 302 primer and coated with SS100 HP/UV. A clear aliphatic topcoat was added to maintain long-term color integrity.

For more pictures please see the following page Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: RESULTS: Project Description: The end user selected the product for use as an anticorrosion agent applied to tank interiors utilized in manufacturing processes that involve liquid solutions with 10-15% acidic content. A 1.5mm coating of HT was applied over sand blasted steel, brick and concrete. A suitable primer was utilized to ensure adhesion to the various surfaces. HT was also used as an interior coating for the tanks acidic gaseous exhaust system, to seal flanged drain piping connections and penetrations and for secondary containment (spill containment) around the perimeter of many of the process tanks. Acid Tanks Manufacturing Anti-Corrosion Chengdu Chemical Corporation Not applicable HT 3200 m2 September 2002 Excellent

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: Rock face encapsulation Mining Construction, anticorrosion Western Mining Not available HT Multiple rock faces 1999 October

INSPECTION RESULTS: Excellent, no visible failure JOB DESCRIPTION: HT was chosen to replace Shot Crete to stabilize rock faces for above and below ground mining applications due to HT’s strength, impact resistance, fast cure times, and generally superior physical characteristics. The rock faces were air blasted to remove loose material and the HT was sprayed directly onto the face. The area was able to be returned to service for continued drilling and blasting almost immediately due to the limited downtime.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: Sewage pit Sewage, waste water, water treatment Anticorrosion South Queensland Sewer Treatment N/A 2 mm SS100 300 m² 1998 November

INSPECTION RESULTS: Excellent JOB DESCRIPTION: SS100 was chosen to protect the concrete of this sewage pit from constant sulphide attack that is always present in sewage applications. SS100 superior physical properties and its limited downtime made it an easy decision for the owner. The concrete was high-pressure water blasted and then primed before SS100 was applied to a 2 mm DFT.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: Waste Storage Tanks Manufacturing Anti-Corrosion Chengdu Chemical Corporation CONTACT: SYSTEM: AREA: COMPLETION: RESULTS: Not applicable HT 1100 m2 August 2002 Excellent

Project Description: The product was selected for use as an anti-corrosion agent applied to open air storage tank interiors utilized for storage of manufacturing waste products in both liquid and solid state. These waste products contain from 7-10% acidic content. A 1.5mm coating of HT was applied over sweet blasted concrete. A suitable primer was utilized to ensure adhesion to the concrete substrate.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: Sewage treatment facilities Sewage, waste water, water treatment Anticorrosion Townsville City N/A Nukote-ST 54 m² 1998 August

USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent JOB DESCRIPTION: ST was chosen to protect the concrete and steal of this sewage treatment facility from constant sulphide attack that is always present in sewage applications. ST superior physical properties and its limited downtime made it an easy decision for the owner. The water level was lowered, the substrate cleaned and coated with 1 mm of ST. The facility remained functional during application, and within hours was back at full production.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: Steel agitators Mining Anticorrosion Placer Pacific Ltd, Kingston Gold Mine Steve Melling, 0417713873 HT 6 mm 120 m² 1998 November

INSPECTION RESULTS: Excellent JOB DESCRIPTION: HT was chosen due to its excellent physical properties, fast cure time, flexibility, and its acid, chemical and wear resistance. The steel agitator was abrasive blasted, primed with 302 primer and coated with 6 mm of HT.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: Steel derrick screens Mining Anticorrosion Placer Pacific, Ltd, Kidston Gold Mine Not available 6 mm HT onto primed steel 30 m² each 1998 September

INSPECTION RESULTS: Excellent JOB DESCRIPTION: The steel surface was abrasive blasted to a 2.5 mm profile and primed. HT was applied to the derrick screens and underpans at a 6 mm dft to protect the steel from both corrosion and abrasion. After twelve months of continued, 24 hour, use the surfaces were inspected and were found free from visible wear or problems. Polyurea has replaced polyurethanes as the coating of choice at this mining facility.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: Steel orifice plate protection Mining Anticorrosion, abrasion resistance Pasminco Mining, Kidston Gold Mine Not available HT Multiple plates 1998 August

OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent, no visible failure JOB DESCRIPTION: abrasion resistance. HT was chosen to coat steel orifice plate covers for anticorrosion and

The plates were abrasive blasted to a 2.5mm profile and primed with 302 primer. HT was applied at a 3 mm dft. The covers have performed extremely well in the rigorous, 24-hour production schedule of this mine.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: Sugar liquor tank Sugar refinary Abrasion resistance, Anticorrosion CSR Refinery Inkerman Sugar Mill Not available 2 mm SS100 300 m² 1998 June

INSPECTION RESULTS: 1999, December-Excellent JOB DESCRIPTION: SS100 was chosen to repair a “beyond repair” sugar liquor tank. The owner hoped to extend its useful life one more season. However, after successfully applying Nukote SS100 the tank has performed as expected for many years beyond the hoped for one year despite the harsh abrasive and corrosive environment. The tank was high-pressure water blasted and then primed. SS100 was applied at 2mm DFT. The owners were not only impressed with the extended useful life of the tank, but also the minimized downtime for application.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: Truck bed Commercial delivery Anticorrosion, impact and slip resistance Sunny Industrial Korea Not available HT Entire bed 1999 August

INSPECTION RESULTS: Excellent JOB DESCRIPTION: HT was chosen due to its excellent physical properties, impact and slip resistance, as well as its anticorrosion properties. The owners are especially pleased with the products performance around salt water. FOR ADDITIONAL PICTURES OF SIMILAR APPLICATIONS PLEASE SEE THE FOLLOWING PAGE

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

Hot asphalt dump bed

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

NUKOTE PROJECT PROFILES
FLOOR APPLICATIONS

NUKOTE COATING SYSTEMS 629 LINGLING ROAD / AIHE MANSION SUITE 7H SHANGHAI, CHINA 200030 TEL: +8621-5424-9811 / FAX: +8621-5424-9815 www.nukote-asia.com

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: CRL Tankhouse Mining Acid and electrolyte anticorrosion MIM Copper Refineries, Townsville Not available 1-2 mm SS100 onto prepared concrete 1,100 m² 1998 June

OWNER:

CONTACT: SYSTEM:

COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent JOB DESCRIPTION: SS100 was chosen because of its ease of application, chemical and acid resistance, slip resistance, flexibility, and abrasion resistance. The minimized downtime was also a great advantage in choosing SS100. The concrete degradation was removed and replaced. SS100 was then applied onto a primed surface at a 1-2 mm dft.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION: RESULTS: Manufacturing Facility Floor Coating Automotive Anti-Corrosion, Anti-Abrasion and Non-Slip General Motors Not applicable Nukote-HT-AL 1450 m2 November 2001 Excellent

PROJECT DESCRIPTION: Nukote Polyurea was used on a variety of floor area at General Motors Shenyang China Facility. The product was selected for its durability, color stability and texture-ability. Standard grey color HT was used in the process control room and paint shop work areas. Standard Sand color HT was used as the base coat in the Climate Controlled CMM Room with AL top coating used in three separate colors of black, safety yellow and red to create designated walk paths, danger striping at automated areas, etc. AL was selected for use in this application due to its abrasion resistance and stable vibrant colors.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: Loading dock Mining Protective floor coating Ernest Henry Mine Not available 1mm ST onto prepared plywood 52 m² 1998 August

OWNER: CONTACT: SYSTEM:

COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent JOB DESCRIPTION: ST was chosen because of its ease of application, chemical and acid resistance, slip resistance, flexibility, and abrasion resistance. In short, ST is a great solution to the rigors a loading dock experiences. The minimized downtime was also a great advantage in choosing ST. The delaminating plywood sheets were sanded, holes filed, and primed. Then ST was applied with a 1 mm dft.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: Workshop floor Mining Protective floor coating Ernest Henry Mine Not available 1mm SS100 onto prepared concrete 120 m² 1998 July

COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent JOB DESCRIPTION: SS100 was chosen because of its ease of application, chemical and acid resistance, slip resistance, flexibility, and abrasion resistance. The minimized downtime was also a great advantage in choosing SS100. The concrete was acid washed and primed. SS100 was then applied onto a primed surface at a 1-2 mm dft.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: Workshop floor-battery store Mining Protective floor coating Ernest Henry Mine Not available 1mm ST onto prepared concrete 1,200 m² 1998 July

INDUSTRY: USE: OWNER: CONTACT: SYSTEM:

COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent JOB DESCRIPTION: ST was chosen because of its ease of application, chemical and acid resistance, slip resistance, flexibility, and abrasion resistance. The minimized downtime was also a great advantage in choosing ST. The concrete was acid washed and primed. ST was then applied onto a primed surface at a 1-2 mm dft.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

NUKOTE PROJECT PROFILES
MARINE APPLICATIONS

NUKOTE COATING SYSTEMS 629 LINGLING ROAD / AIHE MANSION SUITE 7H SHANGHAI, CHINA 200030 TEL: +8621-5424-9811 / FAX: +8621-5424-9815 www.nukote-asia.com

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: Aluminum boat lining Port management AnticorrosionProtective coating for aluminum boat Townsville Port Authority Not available SS100 1.5 mm 15 m² 1999 September

OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent JOB DESCRIPTION: The aluminum boat was cleaned with an abrasive blast and then primed. SS100 was applied to a 1.5 mm dft. SS100’s ability to strengthen and waterproof the boat prevented its being scrapped. The Port Authority can continue to use the boat to inspect the port facilities.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: Buoy coating Shipping, port management Protective coating buoy Marine Institute, Shanghai China Nukote Shanghai Office AMP100 with AE4 additive applied at 2mm multiple buoys 2001 September

COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent JOB DESCRIPTION: The institute usually uses a two coat process that requires up to one week of shore based preparation and application. Using the Nukote systems allowed Shanghai Marine Institute to prepare and recoat the Buoy in just 2 days. Of more critical interest to the institute is the ability of Nukote to withstand much longer design life in the severe ocean conditions. Previous coatings lasted 6 months to one year before excessive deterioration meant the Buoy had to be serviced. Now Nukote can reduce the out of service time by many years per buoy.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

PROJECT PROFILES

Project: Marine Flotation Docks Client: Target Marine Distributor: Nukote Coating Systems Contractor: Target Marine Application Type: Waterproofing-Anti-Corrosion Completion: 2004 Scope: The project provision of Nukote Aromatic and Aliphatic Polyureas and Primers for use in coating of concrete flotation docks manufactured from concrete and foam flotation bases. The pontoons are used in the construction of docks and billets for Navy Vessels and in projects such as Palm Island. System: Surface Area: Completion Date: Results: Target Marine has changed their specification to utilize Nukote products and is currently a registered OEM affiliate of Nukote and certified application company for Nukote products. 100 Microns of Z-Prime with 1000 Microns of Nukote HT with 500 Microns of Nukote AL 212 m2 per dock assembly (hundreds of assemblies) August 2004

SHANGHAI ♦ JAKARTA ♦ DUBAI ♦ SEATTLE ♦ DAFENG ♦ LONG BEACH www.nukote-asia.com [email protected]

PROJECT PROFILES

Project: Navy Corvette Client: Royal Oman Navy Distributor: Nukote Coating Systems Contractor: Nukote Coating Systems Application Type: Corrosion Resistance Completion: 2004 Scope: The project included provision of Nukote Aromatic and Aliphatic Polyureas for use in anti-corrosion and waterproofing of a Navy Gun Boat deck and surfaces. The aluminum checker plate surface was high pressure water blasted to remove existing coatings and contaminants, followed by application of Nukote Z-Prime followed by application of Nukote HT Aromatic Polyurea followed by a color stable coat of Nukote AL with spray applied anti-slip texturing. System: Surface Area: Completion Date: Results: The Royal Oman Navy is completely satisfied resulting in their specifying Nukote products for all marine vessel and dock applications in future. 100 Microns of Z-Prime with 1000 Microns of Nukote HT with 500 Microns of Nukote AL 150 m2 August 2004

SHANGHAI ♦ JAKARTA ♦ DUBAI ♦ SEATTLE ♦ DAFENG ♦ LONG BEACH www.nukote-asia.com [email protected]

PROJECT PROFILES

Project: Marine Buoy Coatings Client: Shanghai Port Authority Distributor: Nukote Coating Systems Contractor: Nukote Coating Systems Application Type: Saltwater Corrosion Resistance Completion: 2001 Scope: Abrasive blast steel buoy surfaces to SA 2.5 anchor profile, prime and coat using Aliphatic Pure Polyurea. The objective is to provide corrosion resistance ultra-violet stable coating ensuring longer service life and reduce maintenance costs System: Surface Area: Completion Date: Results: After more than 3-years of continuous service the coatings remain fully adhered and color stable. Even after damage caused by collisions with vessels the coatings remain adhered and easily repairable. 2000 Microns of Nukote AL Aliphatic Polyurea over 100 Microns of Nukote Metal Prime Per Buoy 52 m2 September 2001-2002

SHANGHAI ♦ JAKARTA ♦ DUBAI ♦ SEATTLE ♦ DAFENG ♦ LONG BEACH www.nukote-asia.com [email protected]

PROJECT PROFILES

Project: Shanghai Wharf Pilings Client: Shanghai Port Authority Distributor: Nukote Coating Systems Contractor: Qingdao Anti Corrosion Services Application Type: Abrasion-Corrosion Resistance Completion: 2004 Scope: High Pressure blast cleaning of existing steel piling surfaces, followed by application of inhibitors to remove impregnated salts, application of primer and coat using Aromatic and Aliphatic Pure Polyurea. The objective is to provide corrosion and abrasion resistance with ultra-violet stable coating ensuring longer service life and reduce maintenance costs. The coating system was applied to splash zone limits at low-tide. System: 500 Microns of Nukote AL Aliphatic Polyurea over 1000 Microns of Nukote ST Aromatic Polyurea over 100 Microns of Nukote Metal Prime 1,800 m2 September 2004

Surface Area: Completion Date: Results:

Fast and easy repair method in difficult application conditions providing protection required by Client.

SHANGHAI ♦ JAKARTA ♦ DUBAI ♦ SEATTLE ♦ DAFENG ♦ LONG BEACH www.nukote-asia.com [email protected]

PROJECT PROFILES

Project: Taiwan Wharf Pilings Client: Taiwan Petrochemical Distributor: Nukote Coating Systems Contractor: Taiwan Paint and Varnish Application Type: Abrasion-Corrosion Resistance Completion: 1999 Scope: The pilings were abrasive blast cleaned to SA 2.5, followed by application of primer and coat using Aromatic Pure Polyurea. The objective is to provide corrosion and abrasion resistance with ultra-violet stable coating ensuring longer service life and reduce maintenance costs. The coating system was applied to complete piling lengths prior to pile driving followed by coating of pile tops after driving and concrete fills. System: Surface Area: Completion Date: Results: No disbondment or fading after more than four-years in service. 2000 Microns of Nukote AL Aromatic Polyurea over 100 Microns of Nukote Metal Prime 15,000 m2 1999

SHANGHAI ♦ JAKARTA ♦ DUBAI ♦ SEATTLE ♦ DAFENG ♦ LONG BEACH www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: Commercial boat coating Marine, petrochemical Anticorrosion Southern Cross Nukote offices, 8621-5424-9811 Interior—HT Exterior-ST base with AL top coat 18,000 m² 2002 December

COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Owner is pleased with both appearance and performance JOB DESCRIPTION: The owner actually had two separate coating needs to protect his investment by extending the boat’s useful life. The primary need was exterior coating. The exterior coating system included a translucent ST base coat with a colored topcoat for both appearance and resistance to the sun’s ultraviolet rays. Pool blue was used above the waterline and light blue was used below the waterline. The interior coating needs were best met using medium gray HT. Required surface preparation includes abrasive blasting removing all rust and previous coating and the application of a primer (especially in areas where the original coating or rust remains). HT can also be used to enhance adhesion. This project was applied by Nukote’s Indonesian distributor, PT Sandvik. Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: Military Vessel Coating Military / Marine Waterproofing, Anti-Abrasion, Anti-Corrosion, Sound Attenuation United States Navy Not applicable Various Polyurea Products Various Various

INSPECTION RESULTS: Excellent

PROJECT DESCRIPTION: Nukote Polyureas have been used by the US Military for many years. The US Navy has recently accepted the products for use as a special vessel coating. Nukote ELP is used as an aircraft carrier deck coating and was selected for its ability to be applied at sea, self-leveling characteristics and durability. Nukote HT was selected for use as a Nuclear Submarine coating for its durability, sound attenuation and spray texture capability (non-slip deck surfaces).

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: Flotation cell launders Chemical processing Anti-corrosion Century Zinc Not available 3 mm SS100 3,652 m² 1999 October 7

INSPECTION RESULTS: Excellent JOB DESCRIPTION: SS100 was applied over existing polyurethane in the launders of 44 flotation cells, which was failing due to severe blistering. The polyurethane was high-pressure water blasted, treated with N-Methyl-Prolidone solvent and washed. Finally, it was coated with 3 mm DFT SS100. The product’s rapid cure time enabled the plant to be commissioned well ahead of schedule saving the owner substantial amounts of money in down time.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: Wharf pylon coating Shipping, port management Wharf pylon anticorrosion Taiwan Petrochemical Not available SS100 at 3 mm dft 1,700 pilings, 115,000 liters 1998 April

INSPECTION RESULTS: Excellent JOB DESCRIPTION: SS100 was applied at 3mm dft over the substrate after sandblasting to a 1 mil anchor profile. The coating pylons were pile driven into the seabed where they have performed without trouble or complaint. The coating’s attributes naturally reject marine borers, which cause substantial damage to most other coatings. This project is expected to perform for 50 years.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: Wharf pylon coating Shipping, port management Wharf pylon anticorrosion/impact resistance Townsville Port Authority Not available SS100 at 1 mm with AE4 Wharf pylons Continuing project, started in 1999 October

OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent JOB DESCRIPTION: SS100 with AE4 was applied over the substrate after washing it with 3,000 psi water. Rusted areas were ground to white metal. SS100’s fast drying time prevented the tide from adversely affecting the coating. SS100 was chosen as a long-term corrosion protection coating because it is tough, flexible, saltwater resistant, and its cure time made it unaffected by tides. Its durability makes it damage resistant from fishing boats that tie up to the wharf.

Please see the following page for additional pictures.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

NUKOTE PROJECT PROFILES
PIPELINE APPLICATIONS

NUKOTE COATING SYSTEMS 629 LINGLING ROAD / AIHE MANSION SUITE 7H SHANGHAI, CHINA 200030 TEL: +8621-5424-9811 / FAX: +8621-5424-9815 www.nukote-asia.com

STEAM PIPE PROFILE
PROJECT: Alaska Petrochemical Valdez Alaska Oil and gas Steam Distribution System Alaska Petrochemical Corporation Not Available Polyurethane Foam/Polyurea HT Composite 28000 Lineal Meters 26” OD Piping and Fittings May 7, 1999

INDUSTRY: USE: OWNER:

CONTACT: SYSTEM:

COATED AREA:

COMPLETION DATE:

INSPECTION RESULTS: No Technical Problems JOB DESCRIPTION: Provided an insulated piping system for use in a steam distribution system located on the Alaska North Slope. Polyurethane foam was applied using Nukote Lathe Technology and then coated with 60 MIL (1.5 mm) of Nukote HT Pure Polyurea. The piping system was installed on both racks and underground. Nukote developed this system in response to the customer’s request for a solution to their extreme temperature and adverse soil conditions. The system provided resolved the customer’s problem while providing an extremely durable and cost effective solution that allowed installation and repair in extreme weather conditions. Nukote Pre-Insulated Piping Systems are a patented Polyurethane Foam/Pure Polyurea composite with unique pipeline insulation and protection capabilities. Contact our sales and technical departments for more details.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

CRUDE OIL PIPELINE PROFILE
PROJECT: Valdez North Slope Oil and gas Oil Flow Line Arco Not Available Insulated Composite 34,000 Lineal Meters June 23, 2000

INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: No Technical Problems JOB DESCRIPTION: Lathe applied Nukote HT over 75mm of multiple densities of Polyurethane Foam Insulation using patented Nukote Coating Systems application equipment. Heat tracing system was incorporated into the composite system. Project was for direct burial and above ground applications of the crude oil flow lines. This project is a standard thermal insulation coating composite application for Nukote Polyureas. Arco selected this Nukote Thermal Systems Composite due to the high physical properties of the coatings, their ability to be applied at extremely low temperatures and the thermal integrity of the completed system. This was the project was undertaken at the owners request for a thermal coating system that could perform well in adverse conditions and reduce costs over traditional double steel with injected insulation piping system. Currently Arco (now BP/Arco) is using this system on an ongoing basis for replacement and repair of the total pipeline. Nukote Thermal Composites offer unique capabilities. Contact our sales and technical departments for more details. Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

NATURAL GAS PIPELINE PROFILE
PROJECT: Suban I Indonesia Oil and gas Natural Gas Well Flow Line Gulf/Conoco Mr. Darryl Berini Anti-Corrosion 18,500 Lineal Meters September 10, 2002

INDUSTRY: USE:

OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: No Technical Problems JOB DESCRIPTION: Lathe applied Nukote HT to straight piping sections using patented Nukote Coating Systems application equipment. Spray applied hot bends and filed joints on ROW. Cold Bends were performed in the field after coating of straight pipe sections with no damage to coating applied prior to bending. Project was direct burial of the Suban natural gas field well flow lines. This project is a standard anti-corrosion application for Nukote Polyureas. Gulf/Conoco selected Nukote HT due to its high physical properties and its ability to withstand constant temperatures of 135 to 150 Celsius. This was the first project for Gulf/Conoco using Nukote products. Currently Gulf/Conoco has written their own specification for Nukote applications and allows its use on all projects undertaken. Nukote Anti-Corrosion Pipe Coatings have unique protection capabilities. Contact our sales and technical departments for more details. Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

NATURAL GAS PIPELINE PROFILE 2
PROJECT: Sumpal Indonesia Oil and gas Natural Gas Well Flow Line Gulf/Conoco Mr. Darryl Berini Anti-Corrosion 5,400 Lineal Meters July 19, 2002

INDUSTRY: USE:

OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: No Technical Problems JOB DESCRIPTION: Lathe applied Nukote HT to straight piping sections using patented Nukote Coating Systems application equipment. Project was for direct burial of the Sumpal natural gas field well flow lines. This project is a standard anti-corrosion application for Nukote Polyureas. Gulf/Conoco selected Nukote HT due to its high physical properties and its ability to withstand constant temperatures of 135 to 150 Celsius. This was the second project for Gulf/Conoco using Nukote products. Currently Gulf/Conoco has written their own specification for Nukote applications and allows its use on all projects undertaken. Nukote Anti-Corrosion Pipe Coatings have unique protection capabilities. Contact our sales and technical departments for more details.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

PROJECT PROFILES

Project: Suban I Client: Conoco Phillips Distributor: Nukote Coating Systems Contractor: Nukote Coating Systems Application Type: Anti Corrosion Completion: 2002 Scope: The Project included provision automated pipe coating facilities in the field on the ROW. The pipe coating included 8-10 and 12 inch diameter carbon steel SAW pipe and field joining after installation. System: Surface Area: Completion Date: Results: Coating completed for 19000 lineal meters of piping within time schedule and in accordance with customer specifications. 1500 Microns of Nukote HT over blast abrasive cleaned steel pipe to SA 2.5. No primer required or utilized. 22,500 m2 October 2002

SHANGHAI ♦ JAKARTA ♦ DUBAI ♦ SEATTLE ♦ DAFENG ♦ LONG BEACH www.nukote-asia.com [email protected]

PROJECT PROFILES

Project: Valdez Trunk Lines Client: ARCO Distributor: Nukote Coating Systems Contractor: Veco Alaska Application Type: Thermal Control & Corrosion Resistance Completion: 2001 Scope: The Project included automated production of thermal insulated piping system coatings utilizing PU foam and Aromatic Polyureas to provide a thermally efficient and durable system for the Client. The system included heat tracing provisions and field jointing of installed pipe sections. System: 200 mm of tow-density polyurethane foam applied over abrasive blast cleaned pipe to SA 2.5 anchor profile. The foam was planed to a perfect circumference and then 1500 Microns of Nukote Minus 40 Aromatic Polyurea was applied to the foam surface. 235,000 m2 August 2001

Surface Area: Completion Date: Results:

No failure instances with product continuing in use for the Client as repairs and retrofits are required.

SHANGHAI ♦ JAKARTA ♦ DUBAI ♦ SEATTLE ♦ DAFENG ♦ LONG BEACH www.nukote-asia.com [email protected]

PROJECT PROFILES

Project: Sumpal I Client: Marubeni Itochu Steel Distributor: Nukote Coating Systems Contractor: Nukote Coating Systems Application Type: Anti Corrosion Completion: 2002 Scope: The Project included provision automated pipe coating facilities in the field on the ROW. The pipe coating included 10” diameter incanal pipe sections coating. System: Surface Area: Completion Date: Results: Coating completed for 6,700 lineal meters of piping within time schedule and in accordance with customer specifications. 1500 Microns of Nukote HT over blast abrasive cleaned steel pipe to SA 2.5. No primer required or utilized. 22,500 m2 October 2002

SHANGHAI ♦ JAKARTA ♦ DUBAI ♦ SEATTLE ♦ DAFENG ♦ LONG BEACH www.nukote-asia.com [email protected]

PROJECT PROFILES

Project: Valdez Process Facilities Client: ARCO Distributor: Nukote Coating Systems Contractor: Veco Alaska Application Type: Thermal Control & Corrosion Resistance Completion: 2002 Scope: The Project included provision of thermal insulated piping system coatings utilizing PU foam and Aromatic Polyureas to provide a thermally efficient and durable system for the Client. The system required production of half-shell components with field installations to equipment system pipes previously installed. System: 200 mm of tow-density polyurethane foam applied over abrasive blast cleaned pipe to SA 2.5 anchor profile. The foam was planed to a perfect circumference and then 1500 Microns of Nukote minus 40 Aromatic Polyurea was applied to the foam surface. 47,000 m2 September 2002

Surface Area: Completion Date: Results:

No failure instances with product continuing in use for the Client as repairs and retrofits are required.

SHANGHAI ♦ JAKARTA ♦ DUBAI ♦ SEATTLE ♦ DAFENG ♦ LONG BEACH www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: Insulated piping Oil and gas Insulated piping system Alaskan petrochemical company EJ Bartells, Renton WA 2 mm Nukote -40 onto #2 polyurethane foam Entire plant steam pipe system 1998 February

INSPECTION RESULTS: Good JOB DESCRIPTION: Members of Nukote Coating Systems invented a patented lathe application system for polyurethane and Nukote polyurea. For this project, Nukote created a special formulation of Nukote polyurea called –40, which was designed especially for sub zero application and use. Since 1998, advances have made it so Nukote’s standard polyureas would work just as well in similar situations. The straight sections of the pipe systems were applied using the patened lathe technology referenced above.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: Potable water pipeline Public utilities, food handling Anticorrosion Confidential by request Norm English, 07-4775-1033 SS100 Pipeline interior and exterior 1997 August

INSPECTION RESULTS: Good JOB DESCRIPTION: SS100 was chosen to coat the interior and exterior of this potable water pipe. The pipe was abrasion blasted to a 1mm profile and the SS100 was applied directly onto the pipe. Coating both sides lengthens the pipe’s useful life by reducing corrosion. The interior coating also helps reduce friction making the pipeline more efficient. Nukote is certified for use with potable water in both Australia and the UK.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: Lathe-applied insulated piping Oil and gas Anticorrsion/insulation Nukote Coating Systems Nukote Shanghai Office As per requirements As per requirements N/A

INSPECTION RESULTS: N/A JOB DESCRIPTION: Nukote technicians and engineers originally designed this proprietary lathe application system to meet the insulated piping needs of the international oil and gas industry. The systems has proved very successful for most other pipeline anticorrosion and insulation needs. For most oil and gas insulated piping, the pipe is first coated with polyurethane foam according to the owner’s required thickness. The foam is planed down to provide a level substrate. The planed foam is then coated with Nukote polyurea as per the owner’s required dft. The coated pipe is ready to be moved and installed within minutes. The in-field joining can be accomplished using polyurethane foam half shells and the Nukote polyurea can be applied using either a standard dual-component spray machine or using Nukote hand-applied polyurea.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

NUKOTE PROJECT PROFILES
PRIMARY CONTAINMENT APPLICATIONS

NUKOTE COATING SYSTEMS 629 LINGLING ROAD / AIHE MANSION SUITE 7H SHANGHAI, CHINA 200030 TEL: +8621-5424-9811 / FAX: +8621-5424-9815 www.nukote-asia.com

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: Chemical Tank Farm Chemical manufacturing Secondary containment, hazardous material containment, Anticorrosion Great Western Chemical Doug Scott, 001-907-488-3555 1 mm SS100 HP/UV on 6” 2# polyurethane foam Two 114,000 liter tanks 1995 June

OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: 1996, December Excellent, slight discoloration JOB DESCRIPTION: The tanks were cleaned and then sprayed with 6” of 2# polyurethane foam for insulation. SS100 at a 1 mm dft was sprayed on top of the foam for an anticorrosion cover. The tank was sprayed with aluminum color. In addition to the tanks, the concrete dykes were sprayed with the same polyurea in black as a secondary containment coating.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: RESULTS: El Segundo Manufacturing Primary Containment US Air Force Nukote Asia ABC /Geotextile 2100 m2 1999 Excellent

Project Description: This tank project required a membrane not an attached liner, due to its construction that included gaps and seams too large to apply directly to the substrate. A geotextile fabric was selected for use as the membrane backing. The fabric was rolled out to overlap at all vertical and horizontal seams and then coated with spray applied ABC Polyurea to a DFT of 2 mm. This application method provides a seamless membrane that can move with expansion and contractions, is entirely waterproof and resistant to acids and alkalis up to 10% content by volume. The exterior of the tank wall to floor interface was also sealed using Seal 100 inject able Polyurea. Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: Deionized water tanks Mining Primary water containment, hazardous material containment Large copper mine based in Utah, USA Brice Westphal, 001-619-236-8928 SS100 1.5-2 mm dft Two 12x8 m tanks 1994 December

OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: 1996, October excellent JOB DESCRIPTION: The concrete tanks were sweep grit blasted and then obvious cracks were filled with epoxy grouting. SS100 was applied at 1.5-2 mm dft. Cracks that had previously caused leaking of the deionized water were sealed and the tanks remain watertight.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

PROJECT PROFILES

Project: Larona Canal Client: PT Inco Indonesia Distributor: Nukote Coating Systems Contractor: Nukote Coating Systems Application Type: Waterproofing Completion: Annual Project Scope: The canal is an integral component of the hydroelectric facilities providing the only power source for this remote nickel mine. The canal is shut for repairs once per year allowing only 3-days of application time for repairs to failing canal construction joints and concrete substrate. The application work is schedule months in advance and completed flawlessly within the annual 72-hour application window. Surface preparation and coating of repaired construction joints and failure areas is accomplished applying Nukote Aromatic Pure Polyurea onto the existing surface profile with no primer. During each of the completed annual repair periods 16,000 liters of product was applied for a total of 48,000 liters through September 2003. System: Surface Area: Completion Date: Results: 1500 Microns of Nukote HT Aromatic Polyurea 15,000 m2 September 2001-2002-2003 No adhesion failure or Disbondment apparent after inspections during each annual repair period.

SHANGHAI ♦ JAKARTA ♦ DUBAI ♦ SEATTLE ♦ DAFENG ♦ LONG BEACH www.nukote-asia.com [email protected]

PROJECT PROFILES

Project: Jiaxing Coal Fire Plant Client: China Power Distributor: Nukote Coating Systems Contractor: Lang Dang Corrosion Co. Application Type: Waterproofing-Corrosion Resistance Completion: 2003 Scope: The Project included internal coating of concrete cooling water tanks, external and internal coating of process tanks and miscellaneous deck and steel component coatings. System: 1000 Microns of Nukote Aromatic HT Polyurea (various colors) over 100 Microns of various primers dependent on substrate type. Decks and walkways included application of 500 Microns spray applied (no broadcast media) texture coat. 39,000 m2 December 2003

Surface Area: Completion Date: Results:

No disbondment or other failures encountered and customer has specified coating systems for all other power plant projects underway in China.

SHANGHAI ♦ JAKARTA ♦ DUBAI ♦ SEATTLE ♦ DAFENG ♦ LONG BEACH www.nukote-asia.com [email protected]

PROJECT PROFILES

Project: Jiangsu Coal Fire Plant Client: Nanjing Power Distributor: Nukote Coating Systems Contractor: Lang Dang Corrosion Co. Application Type: Waterproofing-Corrosion Resistance Completion: 2004 Scope: The Project included internal coating of concrete cooling water tanks, internal and external coating of process tanks and miscellaneous deck and steel component coatings. System: 1000 Microns of Nukote Aromatic HT Polyurea (various colors) over 100 Microns of various primers dependent on substrate type. Decks and walkways included application of 500 Microns spray applied (no broadcast media) texture coat. 22,000 m2 August 2004

Surface Area: Completion Date: Results:

No disbondment or other failures encountered and customer has specified products for use in Phases II and III in 2005-2006.

SHANGHAI ♦ JAKARTA ♦ DUBAI ♦ SEATTLE ♦ DAFENG ♦ LONG BEACH www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: RESULTS: Fire Water Basin Industrial Primary Containment Dow Chemical Charles Zhang Nukote-ST 1500 m2 June 2002 Excellent

Project Description: The new Dow Chemical facility located near Suzhou, China required the construction of a large fire suppression system water holding basin. After construction of the concrete basin the contractor determined that it leaked profusely and was of poor structural integrity. Nukote Polyurea ST was applied to sweet blasted concrete substrate at a DFT of 1.55 mm nominal. A suitable primer was utilized to eliminate out-gassing and resulting pin holing of the coating that is exhibited with new concrete substrates and to provide good adhesion.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: Fiberglass swimming pool Residential construction Primary containment Private residence Not available 1 mm SS100 HP/UV directly onto prepared fiberglass 72 m² 1997 August

COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent JOB DESCRIPTION: SS100 was chosen as a protective coating liner to repair and strengthen the walls and floor of the badly oxidized fiberglass pool. The walls and floor were cleaned, sanded, and prepared by removing osmosis and filling holes with fiberglass bog. The prepared fiberglass was coated with 1 mm dft of SS100. The owners are delighted with the increased life of their pool.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: Hydroponics bases coating Hydroponics, landscaping Primary containment, secondary containment North Queensland Hydroponic Supplies Ian Gregory, 0404-181673 1 mm SS100 molded foam Entire bases, various size 1998 Summer

INSPECTION RESULTS: Excellent JOB DESCRIPTION: The owner chose SS100 to encapsulate the foam hydroponics bases because of its strength, resilience, and waterproofing abilities. The products appearance and ability to be cleaned were also advantages.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: Hydroponics pond Hydroponics, landscaping Primary containment, secondary containment North Queensland Hydroponic Supplies Ian Gregory, 0404181-673 1.5 mm SS100 10 m² 1998 Summer

OWNER:

CONTACT: SYSTEM: COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent JOB DESCRIPTION: The owner chose SS100 to coat their hydroponics ponds because of its strength, resilience, and waterproofing abilities. The products appearance and ability to be cleaned were also advantages. SS100 also worked excellently because it could be applied over multiple substrates including foam, copper, wire mesh, wood, and woven fabric.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: Roman bath Residential construction, plumbing Primary containment Private residence Private residence Nukote ST 4 m² 1998 November

INSPECTION RESULTS: Excellent JOB DESCRIPTION: The owner’s roman bath was leaking due to the low-quality coating product that was used initially. The flexible slip resistant finish also enhanced ST as a coating option. The tile was cleaned with detergent and with Deco Etch. ST was applied at 1 mm DFT directly over the existing tiles. This option provided not only an attractive but cost-effective solution to replacing the tile in the bath.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: Salt-water swimming pool Residential construction Water containment Hot Rock Café, Toolekea Not available 1 mm SS100 HP/UV directly onto prepared concrete 86 m² 1997 November 21

COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent JOB DESCRIPTION: SS100 was chosen as a protective coating liner to repair and strengthen the walls and floor of the salt-water swimming pool because of its flexibility, durability, and ascetic qualities. The previous liner was removed, the concrete was acid washed. Required areas were patched with rapid-set concrete filer. The concrete was primed with PSSF primer. The concrete was coated with 1 mm dft of SS100.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: Salt-water swimming pool Residential construction Water containment Residential Not available 1 mm SS100 HP/UV directly onto prepared concrete 75 m² 1998 April 14

COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent JOB DESCRIPTION: SS100 was chosen as a protective coating liner to repair and strengthen the walls and floor of the salt-water swimming pool because of its flexibility, durability, and ascetic qualities. The previous liner was removed, the concrete was acid washed. Required areas were patched with rapid-set concrete filer. The concrete was primed with PSSF primer. The concrete was coated with 1 mm dft of SS100.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: Seaquarium Dolphin and Whale tank coating Marine science Water containment Miami Seaqaurium Not available 2 mm HT HP/UV onto prepared substrate Multiple tanks 2001

INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent JOB DESCRIPTION: The previous coatings required replacement every six months, which was costly and dangerous to the animals. Nukote polyurea not only provides a seamless waterproof coating that lasts for decades, it also is nontoxic so it will not hurt the animals in any way. The substrate was cleaned of previous coatings, primed and coated with 2 mm HT HP/UV.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: Soft water basin Mining Water containment/ toxin containment Huntsman Chemical Not available 2 mm ST 23,000 ft² 1996 November

OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent JOB DESCRIPTION: The 60 year old tank was leaching soft water into the surrounding area dissolving the concrete surface. The basin was hydro blasted, grouted and primed and then coated with 2 mm of ST.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

NUKOTE PROJECT PROFILES
ROOF SYSTEM APPLICATIONS

NUKOTE COATING SYSTEMS 629 LINGLING ROAD / AIHE MANSION SUITE 7H SHANGHAI, CHINA 200030 TEL: +8621-5424-9811 / FAX: +8621-5424-9815 www.nukote-asia.com

PROJECT PROFILES

Project: Dubai Creek Client: Dubai Municipality Distributor: Al Gurg Fosroc Contractor: Nukote Coating Systems Application Type: Architectural Roofing Systems Completion: 2004 Scope: The Project included provision of Nukote Aromatic ST and Nukote Polyaspartic PA I with Nukote Z-Primer and application of the products to the incredibly difficult landmark building in Dubai UAE. The project was a renovation that required abrading existing acrylic coatings (that had failed) application of primer at 100 Microns, Aromatic base coat at 700 Microns and Polyaspartic top coat at 250 Microns. System: Surface Area: Completion Date: Results: The composite system provides a durable, color stable coating to handle the harsh desert climate. 1000 Microns of Nukote products composite which included Z-Prime, ST and PA I. 6,000 m2 September 2004

SHANGHAI ♦ JAKARTA ♦ DUBAI ♦ SEATTLE ♦ DAFENG ♦ LONG BEACH www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE

PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: RESULTS:

Roofing System Automotive Manufacturing General Motors Not applicable Nukote-HT 30000 m2 November 2001 Excellent

PROJECT DESCRIPTION: General Motors Manufacturing Facility in Shenyang China is a conglomeration of several buildings, which compromise their Chevrolet Light Truck Production Plant. The existing roofing system was cast concrete with applied insulation and bituminous membrane. The new roof system comprised a complex variety of materials including metal, EPDM and Nukote Coating Systems. Nukote HT was utilized on all parapet to flashing interfaces. The entire perimeter parapet area was encapsulated to eliminate failing concrete falling onto the new glass façade that covered the building perimeter. Nukote Polyureas were also utilized in all gutter drains and around many penetrations throughout the facility.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE

PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: RESULTS:

Roofing System Entertainment Stadium City of Tacoma Not applicable Nukote ST 50000 m2 1999 Excellent

PROJECT DESCRIPTION: The Tacoma Dome is a stadium structure with a heavy structural ridge design component. These ridges give the dome its distinctive look but were a major problem for roofing membrane designers. The slope and valleys within the ridge system were a design problem for conventional roofing system. Polyurea was the ideal solution due to its shape conforming spray application characteristics. Removal of the old roofing membrane to the concrete substrate was followed by application of a polymer primer and then 1.5mm of ST. A white polymeric top coating was then roll applied to provide enhanced ultra-violet resistance.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
CONTACT: PROJECT: INDUSTRY: USE: OWNER: Roofing System Entertainment Stadium City of New Orleans SYSTEM: COATED AREA: COMPLETION DATE: RESULTS: Not applicable SS-HPUV 750000 m2 1998 Excellent

PROJECT DESCRIPTION:

The Super Dome is a stadium structure with a dome design component. This dome design give the stadium it’s distinctive look but became a major obstacle for roofing membrane designers. The slope and radius within the dome system were a design problem for conventional roofing systems. Polyurea was the ideal solution due to its shape conforming spray application characteristics. Removal of the old roofing membrane to the concrete substrate was followed by application of a polymer primer and then 1.5mm of SS-HPUV (Sand Color). This system has been in service for more than four years with no maintenance or repair instances recorded.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: RESULTS: Roofing Systems Various Various Various Not applicable Various Nukote Products Various Various Excellent

PROJECT DESCRIPTION: Nukote Polyureas are simple to apply in roofing applications. The spray applied form fitting nature of the product makes it ideal for roofing surfaces with variable shapes, slopes and interfaces that are difficult for standard roofing materials to be applied to. These characteristics are not the only reason that owners, architects and contractors choose Nukote products for their roofing solution needs. Hydrophobic nature (water does not affect the curing process), fast cure time, durability and total cost are other primary reasons Nukote products are utilized. Nukote Polyureas simply provide a total cost effective solution to most roofing applications and substrates. Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

NUKOTE PROJECT PROFILES
SECONDARY CONTAINMENT APPLICATIONS

NUKOTE COATING SYSTEMS 629 LINGLING ROAD / AIHE MANSION SUITE 7H SHANGHAI, CHINA 200030 TEL: +8621-5424-9811 / FAX: +8621-5424-9815 www.nukote-asia.com

PROJECT PROFILES

Project: Inco Secondary Containment Client: PT Inco Indonesia Distributor: Nukote Coating Systems Contractor: Nukote Coating Systems Application Type: Secondary Containment Completion: 2003 Scope: The Project included provision of geotextile propylene mesh and Nukote ST Aromatic Polyurea and installation of the mesh throughout a containment burm surrounding fuel storage tanks. The mesh was coated with 1000 Microns of ST with no primer required or utilized. System: Surface Area: Completion Date: Results: Coating and Geotextile composition works so efficiently that Client has procured equipment and material to apply their internal works in containment on an ongoing basis. 1000 Microns of Nukote HT over geotextile mesh fabric. 7,500 m2 September 2003

SHANGHAI ♦ JAKARTA ♦ DUBAI ♦ SEATTLE ♦ DAFENG ♦ LONG BEACH www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: Chemical spill containment Chemical manufacturing, mining Secondary containment, hazardous material containment, Queensland Nickel, Ltd. Steven Melling, 1-2 mm Nukote-ST 120 m² 1998 August

OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent JOB DESCRIPTION: ST was chosen to protect the concrete from constant spilling of cobalt, acids, and ammonias. ST's chemical and acid resistant, flexibility, anti slip, and ease of application properties made it an ideal choice. The area was high-pressure water blasted, primed and coated with 1-2mm of ST

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: RESULTS: Various Industrial Secondary Containment Various N/A Various Polyureas Various Various Excellent

Project Description: The combination of Geotextile fabrics with Polyurea coating are fast becoming the preferred choice for secondary containment in many applications. The geotextile fabric is laid out with overlapping seams around the desired perimeters. Penetrations of pipes or other obstacles are easily cut around, rolling the fabric above grade and tight to the penetration or obstacle. The entire surface area is then coated with a Polyurea to the desired DFT and a seamless watertight membrane is established. Note that new mesh products provide even more durable bases then geotextile fabrics and allow for lower DFT applications thus reducing overall costs while maintaining quality. Contact you’re nearest Nukote representative for details. SEE MORE PHOTOS OF THIS APPLICATION ON FOLLOWING PAGE Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: RESULTS: Eielson Air Force Base Military Secondary Containment US Air Force N/A SS 1600 m2 1998 Excellent

Project Description: This project was undertaken as an environmental measure to assure that aviation fuel spills were channeled to a hazardous waste retention tank without contaminating ground water. The project entailed coating a concrete channels interior and exterior with Polyurea SS at a DFT of 2.0 mm. Surface preparation included sandblasting and “grouting of bug holes”, prior to application of a suitable primer.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: RESULTS: Sludge Pits Oil and Gas Secondary Containment BP N/A Nukote-XT 725 m2 2002 Excellent

Project Description: Their contractor Alyeska Pipeline Company in Valdez Alasksa performed this secondary containment project for British Petroleum. The project entailed coating concrete sludge head pits to prevent spills or contamination. Surface preparation was standard with sweet blasting, grouting of bug holes and priming prior to application of XT to the surface. XT is a polyurea designed for higher resistance to hydrocarbons thus making it an excellent choice for secondary containment of petroleum products. Contact you’re nearest Nukote representative for details.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: Chemical Tank Farm Chemical manufacturing Secondary containment, hazardous material containment, Anticorrosion Great Western Chemical Doug Scott, 001-907-488-3555 1 mm SS100 HP/UV on 6” 2# polyurethane foam Two 114,000 liter tanks 1995 June

OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: 1996, December Excellent, slight discoloration JOB DESCRIPTION: The tanks were cleaned and then sprayed with 6” of 2# polyurethane foam for insulation. SS100 at a 1 mm dft was sprayed on top of the foam for an anticorrosion cover. The tank was sprayed with aluminum color. In addition to the tanks, the concrete dykes were sprayed with the same polyurea in black as a secondary containment coating.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: Chemical transload facility Chemical manufacturing Secondary containment, hazardous material containment Great Western Chemical Doug Scott, 001-907-488-3555 1+ mm SS100 with HP/UV additive 1,500 ft² 1994 Spring

INSPECTION RESULTS: No reported problems JOB DESCRIPTION: Great Western had a new concrete containment cell that needed protection against a variety of chemicals that were being transferred from rail tank cars to over-theroad carriers. They reported the most aggressive chemical they expected to transport was 80% hydrochloric acid. To test SS100 performance with such a high concentration a cardboard box was coated and filled with 80% hydrochloric acid. After 7 days the coated showed signs of deterioration. Great Western decided to use SS100 because federal laws require a spill of 80% hydrochloric acid be cleaned up within 24 hours.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: Copper refinery spill containment Mining Acid and organic spills containment Queensland Copper Refineries, Townsville Not available 2 mm ST geotextile fabric COATED AREA: COMPLETION DATE: 50 m² 1998 July 1

CONTACT: SYSTEM:

INSPECTION RESULTS: Excellent JOB DESCRIPTION: ST was the only choice to contain acid and organic spills because the concrete substrate was soaked with oil and wax preventing adhesion of other coating products. ST's flexibility, elongation, chemical resistance, and ability to adhere and provide a waterproof membrane over geotextile fabric. Using the geotextile fabric a seamless membrane was created without the need for adhesion to the substrate. The application was so successful it reduced what would have been a 28-day downtime to 24 hours saving the owner substantial amounts of money.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: Containment of electrolyte pit and floors Mining Anti-corrosion Queensland Copper Refineries, Townsville Not available 2 mm SS100 HP/UV 500+ m² 1998 July 29

INDUSTRY: USE: OWNER:

CONTACT: SYSTEM: COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent SS100 was chosen over existing polyethylene systems, which had JOB DESCRIPTION: previously failed allowing electrolyte and other acids to penetrate and contaminate the concrete. The contaminated concrete was scabbled out and topped with a cement repair mixture. The surface was primed with multiprime and then coated with SS100 with a 2 mm dft. The flexibility, toughness, acid resistance and minimum downtime enabled the area to be back in service within hours.

For more pictures please see the following page Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: Hydro Cracker seal boxes and crude unit seal boxes Oil and gas, petrochemical Secondary containment, hazardous material containment Tesoro Alaska Ray Angel, 001-907-262-5655 2-2.5 mm SS100 on 1” 3# polyurethane foam 20, 2 x 5 meter tanks 1995 August

INSPECTION RESULTS: 1996, Excellent, no problems JOB DESCRIPTION: SS100 was chosen to replace the customized drop-in liners previously used because they typically leaked around the penetrations and piping. The concrete surfaces were steam cleaned and piping was grit blasted. Approximately 1” of 3# polyurethane foam was applied to smooth irregularities in the concrete. SS100 was applied to 2-2.5 mm dft. SS100 sealed the seams, including around the penetrating piping, without any problem. The pits contain water and steam from the hydro cracker as well as jet fuel, crude oil, gasoline, naptha, and dissolved sulfuric acid. Temperatures range from 0° to 149°.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: Tank farm secondary containment Oil and gas Secondary containment Petro Marine Incorporate, Alaska, USA Wyatt Rankin, 001-907-746-5195 SS100 2.5 mm 70,000 ft² 1996

INDUSTRY: USE: OWNER:

CONTACT: SYSTEM: COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent JOB DESCRIPTION: A direct quote from a Petro Marine project manager, “After looking for several years into liners for tank farms, we have found this to be the best liner on the market today. It has the advantage of not having to have a sand covering on top, which will give us 100% monitoring ability daily and the ability to clean up any fuels without contaminating the ground cover over a buried liner. The second reason this liner is superior is we can visually examine the integrity of the liner at anytime. There is not a buried liner anywhere that can be examined or determined to be leak tight. In most cases on seamed, rolled liners the seams start coming off in a couple of years.” The project involved four tank farms throughout Alaska, USA each farm containing numerous tanks and piping for a variety of fuels. All floors and walls are concrete and were covered with 2.5 mm of SS100 over geo-textile fabric. The perimeter of the metal tanks were abraded, primed and masked to .3 m from the ground. The geo-textile was used to counter-flash of the tank chines as an expansion joint. SS100 was then sprayed to the masked line on the tank. Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

NUKOTE PROJECT PROFILES
WATERPROOFING APPLICATIONS

NUKOTE COATING SYSTEMS 629 LINGLING ROAD / AIHE MANSION SUITE 7H SHANGHAI, CHINA 200030 TEL: +8621-5424-9811 / FAX: +8621-5424-9815 www.nukote-asia.com

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: Beaucatcher Tunner Construction Protective lining, waterproofing North Carolina Department of Transportation Terry L. LaDuke, 011-704-452-7030 1.3mm SS100 onto prepared concrete 7,987 m² 1997 July Before

INSPECTION RESULTS: Excellent JOB DESCRIPTION: Sixty-eight year old concrete tunnel was renovated to repair aging concrete and reduce water leakage. The entire tunnel was sandblasted, cleaned with a high-pressure wash and then primed. SS100 was then applied at a 1.3 mm dft. After The NC DOT choose to use Nukote polyurea because of its ability to preserve and extend the useful life of the concrete. It is also easily cleaned with high-pressure water, which reduces maintenance costs. Nukote polyurea is also resistant to graffiti.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

PROJECT PROFILES

Project: Hong Kong Metro Tunnel Client: Hong Kong Municipality Nukote Affiliate: Fosroc Hong Kong Application Type: Waterproofing Completion: 2000 Scope: Application of Aromatic Polyurea over newly poured concrete. The Clients construction schedule required immediate coating without waiting for normal 28-day concrete cure time. A special Fosroc primer was applied directly to the substrate, to encapsulate the “green” concrete eliminating vapor entrapment and the potential for pin-holing of the finished surface. System: Surface Area: Completion Date: Results: 200 Microns of Primer with 1500 Microns of Aromatic Pure Polyurea Top Coat 12,000 m2 August 2000 The completed coated areas were buried within 24-hours of coating application completion. The Tunnels have been in service since January 2001 with no leaking or moisture transmission evident.

SHANGHAI ♦ JAKARTA ♦ DUBAI ♦ SEATTLE ♦ DAFENG ♦ LONG BEACH www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: RESULTS: Project Description: A bullet train was being constructed in Japan. 70% of the project is above grade using tunnels, trestles, etc., to resolve the terrain problems. The problem was deciding what product could most effectively provide the waterproofing features desired and be cost effective. The solution was to use ST Polyurea @ 1.5mm DFT with high pigment loading and ultraviolet inhibitors. Surface preparation was standard sandblasting, grouting of bug holes and use of a suitable primer. Contact you’re nearest Nukote representative for details. Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected] Bullet Train Transportation Waterproofing Japan Nukote Nukote-ST 26000 m2 2001 Excellent

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: RESULTS: Irrigation Flumes Agriculture Waterproofing WAG Nukote HT 1100 m2 1998 Excellent

Project Description: An ancient steel irrigation flume was rusted so badly that 70% of the water it was designed to carry was lost in transit. The solution was to carefully remove as much oxidation as possible by sandblasting. Devoe 167 primer was then applied for adhesion (and because of the primers ability to solidify remaining rust and stop further oxidation). The surface preparation was then followed by spray application of Polyurea HT to a 2.0mm DFT. Contact you’re nearest Nukote representative for details.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: Fountain of the Flags coating Monument or construction maintenance Primary water containment, ascetic appearance University of Alaska, Fairbanks Rick Rocheleau, 907-456-7361 SS100 HP/UV 3,000 ft² 1995 August

USE:

OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: 1996, summer excellent, no loss of water, no discoloration JOB DESCRIPTION: Cracks in the original epoxy coating were leaking thousands of gallons of water per day. After the SS100 application, the fountain is watertight.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: Fountains / Waterfalls / Ponds Entertainment Commercial / Residential / Hospitality Various Not applicable PU Foam / Nukote HM Various Various

INSPECTION RESULTS: Excellent

PROJECT DESCRIPTION: Hotels, Parks, Office Buildings and Theme Parks have been utilizing composites of polyurethane foam and polyurea for several years. These composites are used to construct waterfalls, pools, fountains and related sculptures quickly and easily. Polyurethane foam is sprayed or poured, then sculpted into the desired shape, then coated with High Modulus (Rigid) Polyurea for waterproofing and durability. The coating is then painted with urethane paints to any color or combination of colors desired. Next time you lounge around the pool at your favorite hotel or view and fountain or waterfall display you are most likely looking at an illusion created using Nukote Products. Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: Hong Kong Metro Tunnel Construction Waterproofing/ backfill protection Hong Kong Government Not available 1mm SS100 onto prepared concrete entire tunnel section 2001

OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent JOB DESCRIPTION: SS100 replaced asphalt and plywood for waterproofing and backfill protection. The concrete was cleaned and primed and the SS100 was applied at a 1 mm dft.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: Seaquarium Dolphin and Whale tank coating Marine science Water containment Miami Seaqaurium Not available 2 mm HT HP/UV onto prepared substrate Multiple tanks 2001

INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent JOB DESCRIPTION: The previous coatings required replacement every six months, which was costly and dangerous to the animals. Nukote polyurea not only provides a seamless waterproof coating that lasts for decades, it also is nontoxic so it will not hurt the animals in any way. The substrate was cleaned of previous coatings, primed and coated with 2 mm HT HP/UV.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: Salt-water swimming pool Residential construction Water containment Residential Not available 1 mm SS100 HP/UV directly onto prepared concrete 75 m² 1998 April 14

COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent JOB DESCRIPTION: SS100 was chosen as a protective coating liner to repair and strengthen the walls and floor of the salt-water swimming pool because of its flexibility, durability, and ascetic qualities. The previous liner was removed, the concrete was acid washed. Required areas were patched with rapid-set concrete filer. The concrete was primed with PSSF primer. The concrete was coated with 1 mm dft of SS100.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: Salt-water swimming pool Residential construction Water containment Hot Rock Café, Toolekea Not available 1 mm SS100 HP/UV directly onto prepared concrete 86 m² 1997 November 21

COATED AREA: COMPLETION DATE:

INSPECTION RESULTS: Excellent JOB DESCRIPTION: SS100 was chosen as a protective coating liner to repair and strengthen the walls and floor of the salt-water swimming pool because of its flexibility, durability, and ascetic qualities. The previous liner was removed, the concrete was acid washed. Required areas were patched with rapid-set concrete filer. The concrete was primed with PSSF primer. The concrete was coated with 1 mm dft of SS100.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

NUKOTE PROJECT PROFILES
MISCELLANEOUS APPLICATIONS

NUKOTE COATING SYSTEMS 629 LINGLING ROAD / AIHE MANSION SUITE 7H SHANGHAI, CHINA 200030 TEL: +8621-5424-9811 / FAX: +8621-5424-9815 www.nukote-asia.com

PROJECT PROFILES

Project: Killer Whale Stadium Client: Seaquarium Distributor: Nukote Coating Systems Contractor: Magines Coatings Application Type: Corrosion Resistance Completion: 2003 Scope: The project included renovation of existing tanks, decks, bleachers, walkways and other concrete and steel surfaces of the venue. Combinations of products were used including Aromatic, Aliphatic and Aspartic Polyureas. System: 1000 Microns of Nukote Aromatic HT Polyurea over 100 Microns of various primers dependent on substrate type. 500 Microns of Aliphatic or 200 Microns of Aspartic Polyurea top coats used for color stabilization dependent on area of use 19,000 m2 April 2003

Surface Area: Completion Date: Results:

No disbondment or fading after more than one-year of continuous service. Easily cleaned and maintained during bi-monthly service periods.

SHANGHAI ♦ JAKARTA ♦ DUBAI ♦ SEATTLE ♦ DAFENG ♦ LONG BEACH www.nukote-asia.com [email protected]

PROJECT PROFILES

Project: General Motors Shenyang Client: Jinbei General Motors Distributor: Nukote Coating Systems Contractor: Shenyang Lianguang Application Type: Insulated Waterproofing Composite Completion: 2001 Scope: The Project included provision of Nukote Polyurethane Spray Foam Insulation and Nukote HT Aromatic Polyurea. GM required insulating the climate controlled paint shop from the harsh Northern China winter to eliminate condensation problems. Nukote provided a composite system that accomplished the requirement using 2# PU spray foam applied directly to the concrete wall with no primer required. The PU foam was top coated with Nukote HT. System: Surface Area: Completion Date: Results: The composite system provides a durable, thermally efficient system to handle the harsh climate. 3 Inches of 2# PU Foam with 1500 Microns of Nukote HT 16,000 m2 July 2001

SHANGHAI ♦ JAKARTA ♦ DUBAI ♦ SEATTLE ♦ DAFENG ♦ LONG BEACH www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: RESULTS: Project Description: Many manufacturing processes require insulated storage tanks either during processing or for storage of the completed product. Application of insulation and then shielding the insulation from weather, moisture, etc., with aluminum or steel has been the common method utilized in the past. Pre-insulated composites that use spray applied polyurethane foam and polyurea outer jacketing are fast making the older method obsolete. Spray applied polyurethane foam is one of the best insulators available, far exceeding fiberglass, mineral wool or other standard insulation medias. The foam adheres readily to steel or concrete surfaces without primers and is inexpensive. Polyurea chemically crosslinks with polyurethane foams providing a strong bond without primers as well. This system is durable, efficient and cost effective while providing long life expectancy to the end user. Contact your Nukote representative to calculate insulation and coating thickness required for your projects specific needs. Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected] Insulated Tanks Manufacturing Primary Containment Multiple Multiple Polyurea / Foam Various Various Excellent

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: RESULTS: Project Description: This manufacturing process required insulated tanks for storage of the completed product. Spray applied PU foam with an outer jacket of Polyurea SS was utilized as the best solution for this project. A 3” layer of 2# polyurethane foam was applied directly to the steel substrate with no primer required. 1.5mm of Polyurea ST has then sprayed on top of the foam, again with no requirement for a primer to achieve a strong bond of the Polyurea to the foam. Contact your Nukote representative to calculate insulation and coating thickness required for your projects specific needs. Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected] Insulated Tanks Manufacturing Primary Containment Johns Manville Nukote Asia Polyurea / Foam 12000 m2 2000 Excellent

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: Disney / MGM / Theatres Entertainment Theatre / Theme Park / Stage Sets Various Not applicable PU Foam / Nukote HM Various Various

INSPECTION RESULTS: Excellent

PROJECT DESCRIPTION: The entertainment industry has been utilizing composites of polyurethane foam and polyurea for several years. These composites are used to construct lightweight and durable facades, sculptures and sets quickly and easily. Polyurethane foam is sprayed or poured, then sculpted into the desired shape, then coated with High Modulus (Rigid) Polyurea for waterproofing and durability. The coating is then painted with urethane paints to any color or combination of colors desired. Next time you stay at the MGM Grand in Las Vegas, visit Disneyland or Disneyworld, or attend the opera or theatre you are most likely looking at an illusion created using Nukote Products.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: Displays and Facades Industrial, Hospitality and Construction Architectural Various Not applicable PU Foam / Nukote HM Various Various

INSPECTION RESULTS: Excellent

PROJECT DESCRIPTION: Contractors and Display Companies have been utilizing composites of polyurethane foam and polyurea for several years. These composites are used to construct displays and facades quickly and easily. Polyurethane foam is sprayed or poured, then sculpted into the desired shape, then coated with High Modulus (Rigid) Polyurea for waterproofing and durability. The coating is then painted with urethane paints to any color or combination of colors desired. Next time you admire a stonewall, trade show display or the ambiance of your favorite restaurant you are most likely looking at an illusion created using Nukote Products.

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: RESULTS: Project Description: For the food processing industry, cold storage is a critical part of their business. Reducing energy costs while providing efficient, durable and easily cleanable storage for processed goods is of primary concern. The use of spray applied PU Foam with Polyurea has provided important solutions to this industry over the past decade. Polyurethane foam is one of the most energy efficient insulators available. PU foam readily adheres to concrete and steel, is pour able, inject able and spray able and bonds with polyureas without the need for primers. These characteristics allow conversion of concrete, wood or steel structures for use as cold storage at minimal costs. The seamless polyurea surface is approved for use with food contact by the USDA and is steam cleanable. Polyurea can be applied at the coldest temperatures yet there are several cold application foam and polyurea formulations designed specifically for this industry. Contact you’re nearest Nukote representative for details. Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected] Cold Storage Applications Food Processing Insulation & Coating Various Nukote Foam / Polyureas Various Various Excellent

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: RESULTS: Project Description: Radar dome installations located in a remote area of Alaska were encountering condensation problems. With extremely cold exterior temperatures and ambient room temperatures within the domes, condensation was a major problem. Osmosis via the aluminum shell was too conducive to condensation. The resolution was to coat the exterior of the domes with HT Polyurea at a DFT of 1.5mm. The membrane isolated the aluminum parts from each other and eliminated the condensation problem without affecting the performance of the radar systems. Contact you’re nearest Nukote representative for details. Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected] Radar Domes Military Special US Air Force Nukote HT 7200 m2 1996 Excellent

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: RESULTS: Project Description: NASA had a problem. The satellites they were putting in orbit were primarily built in California. The launch facilities were primarily located in Florida. The US Air Force C3 Transport Aircraft performed transportation of the completed satellites, but in the event of an airline malfunction how could they protect the satellites. A C3 aircraft costs several million dollars. A single satellite can cost 100 times as much. The solution was to construct special fiberglass ejection pods, coat them with Polyurea HT and provide for the satellites to be ejected and parachuted to safety. Contact you’re nearest Nukote representative for details. Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected] Satellite Pods Space Special NASA Nukote HT 2200 m2 1999 Excellent

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: RESULTS: Project Description: GM had a problem. OSHA identified asbestos content in the occluded glass relights around the perimeter of a Pontiac Michigan plant. The asbestos had to be removed or encapsulated for worker safety. Either option caused major plant shut downs to accomplish and great expense. The solution provided was to use CAP Polyurea (translucent) to encapsulate the glass while allowing the relights to function as originally designed. Due to the no VOC characteristics of CAP Polyurea and the fast application nature of the product, the application caused minimal down time for GM (the plant remained open throughout the application) and OSHA was satisfied. Contact you’re nearest Nukote representative for details. Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected] GM Glass Manufacturing Asbestos Encapsulation General Motors Nukote CAP 1600 m2 1999 Excellent

POLYUREA PROJECT PROFILE
PROJECT: INDUSTRY: USE: OWNER: CONTACT: SYSTEM: COATED AREA: COMPLETION DATE: RESULTS: Project Description: BP had a problem. The soil condition in Northern Alaska is very unstable due to the permanent frozen sub soils (permafrost). The topsoil layers freeze and thaw dependent on seasons and temperature swings and mud/slush slides are not uncommon. When these slides occur adjacent to the main Alaska Crude Oil Pipeline and can cause major disruptions in the flow of oil with the associated environmental contamination, a solution had to be found. The solution provided was to use geotextile fabric with Polyurea and sand bagging on slopes adjacent to the pipeline. The result was the end of the problem. Contact you’re nearest Nukote representative for details. Valdez ROW Various Erosion Control BP Nukote HT 1200 m2 2002 Excellent

Suite 7H Aihe Mansion, No. 629 Lingling Road Shanghai, China, 200030 (Tel) 021-5424-9811 (Fax) 021-5424-9815 www.nukote-asia.com [email protected]